SBR rubber sheet is a synthetic rubber product made from styrene and butadiene. It has good abrasion resistance, impact resistance, and low temperature flexibility, as well as moderate aging and weathering resistance. SBR rubber sheet is widely used in the construction, automotive, and industrial sectors for applications such as gaskets, seals, flooring, and conveyor belts.
SBR-01
Property | Value |
Polymer | SBR/NR |
Color | Black |
Density | 1.5 +/-0.05 g/cm3 |
Hardness | 70 +/-5 Shore A |
Tensile Strength | ≥4 MPa |
Elongation at Break | ≥200% |
Working Temperature | -20 to 70 ℃ |
SBR-02
Property | Value |
Polymer | SBR/NR |
Color | Black |
Density | 1.5 +/-0.05 g/cm3 |
Hardness | 60 +/-5 Shore A |
Tensile Strength | ≥5 MPa |
Elongation at Break | ≥250% |
Working Temperature | -30 to 80 ℃ |
SBR-03
Property | Value |
Polymer | SBR/NR |
Color | Black |
Density | 1.3 +/-0.05 g/cm3 |
Hardness | 65 +/-5 Shore A |
Tensile Strength | ≥10 MPa |
Elongation at Break | ≥350% |
Working Temperature | -35 to 85 ℃ |
SBR rubber sheet is a synthetic rubber product made from styrene and butadiene. It has good abrasion resistance, impact resistance, and low temperature flexibility, as well as moderate aging and weathering resistance. SBR rubber sheet is widely used in the construction, automotive, and industrial sectors for applications such as gaskets, seals, flooring, and conveyor belts.
SBR-01
Property | Value |
Polymer | SBR/NR |
Color | Black |
Density | 1.5 +/-0.05 g/cm3 |
Hardness | 70 +/-5 Shore A |
Tensile Strength | ≥4 MPa |
Elongation at Break | ≥200% |
Working Temperature | -20 to 70 ℃ |
SBR-02
Property | Value |
Polymer | SBR/NR |
Color | Black |
Density | 1.5 +/-0.05 g/cm3 |
Hardness | 60 +/-5 Shore A |
Tensile Strength | ≥5 MPa |
Elongation at Break | ≥250% |
Working Temperature | -30 to 80 ℃ |
SBR-03
Property | Value |
Polymer | SBR/NR |
Color | Black |
Density | 1.3 +/-0.05 g/cm3 |
Hardness | 65 +/-5 Shore A |
Tensile Strength | ≥10 MPa |
Elongation at Break | ≥350% |
Working Temperature | -35 to 85 ℃ |