HNBR rubber sheet has good thermal stability, oil resistance, acid and alkali resistance and ozone resistance, and also has good mechanical strength and wear resistance. Widely used in automobile, machinery, chemical industry and other fields. Compared with other rubber sheets, HNBR rubber sheets have better thermal stability and oil resistance, but the price is relatively high.
HNBR-01
Property | Value |
Hardness | 70 +/-5 Shore A |
Density | 1.2 +/-0.05 g/cm3 |
Tensile Strength | ≥20 MPa |
Elongation at Break | ≥500% |
Tear Resistance | ≥45 N/mm |
Abrasion Resistance at 5N | ≤65mm³ |
Working Temperature | -30 to 160 ℃ |
HNBR-02
Property | Value |
Hardness | 70 +/-5 Shore A |
Density | 1.25 +/-0.05 g/cm3 |
Tensile Strength | ≥15 MPa |
Elongation at Break | ≥450% |
Tear Resistance | ≥40 N/mm |
Abrasion Resistance at 5N | ≤80mm³ |
Working Temperature | -30 to 160 ℃ |
HNBR-03
Property | Value |
Hardness | 70 +/-5 Shore A |
Density | 1.4 +/-0.05 g/cm3 |
Tensile Strength | ≥10 MPa |
Elongation at Break | ≥400% |
Tear Resistance | ≥20 N/mm |
Abrasion Resistance at 5N | ≤150mm³ |
Working Temperature | -30 to 160 ℃ |
HNBR rubber sheet has good thermal stability, oil resistance, acid and alkali resistance and ozone resistance, and also has good mechanical strength and wear resistance. Widely used in automobile, machinery, chemical industry and other fields. Compared with other rubber sheets, HNBR rubber sheets have better thermal stability and oil resistance, but the price is relatively high.
HNBR-01
Property | Value |
Hardness | 70 +/-5 Shore A |
Density | 1.2 +/-0.05 g/cm3 |
Tensile Strength | ≥20 MPa |
Elongation at Break | ≥500% |
Tear Resistance | ≥45 N/mm |
Abrasion Resistance at 5N | ≤65mm³ |
Working Temperature | -30 to 160 ℃ |
HNBR-02
Property | Value |
Hardness | 70 +/-5 Shore A |
Density | 1.25 +/-0.05 g/cm3 |
Tensile Strength | ≥15 MPa |
Elongation at Break | ≥450% |
Tear Resistance | ≥40 N/mm |
Abrasion Resistance at 5N | ≤80mm³ |
Working Temperature | -30 to 160 ℃ |
HNBR-03
Property | Value |
Hardness | 70 +/-5 Shore A |
Density | 1.4 +/-0.05 g/cm3 |
Tensile Strength | ≥10 MPa |
Elongation at Break | ≥400% |
Tear Resistance | ≥20 N/mm |
Abrasion Resistance at 5N | ≤150mm³ |
Working Temperature | -30 to 160 ℃ |